Patent application number | Description | Published |
20110027590 | Sequentially Biaxially-Oriented Polyglycolic Acid Film, Production Process Thereof and Multi-Layer Film - A production process of a sequentially biaxially-oriented polyglycolic acid film, which includes Step 1 of stretching an amorphous polyglycolic acid sheet in one direction at a stretching temperature within a range of from 40 to 70° C. and a primary draw ratio of 2.5 to 7.0 times, thereby forming a uniaxially oriented film; Step 2 of causing the uniaxially oriented film to pass through within a temperature environment controlled to a temperature within a range of from 5 to 40° C. and lower by at least 5° C. than the stretching temperature in Step 1; Step 3 of stretching the uniaxially oriented film in a direction perpendicular to the stretching direction in Step 1 at a stretching temperature within a range of from 35 to 60° C. and higher by at least 3° C. than the temperature in Step 2, thereby forming a biaxially oriented film, the area stretch ratio of which is 11 to 30 times; and Step 4 of subjecting the biaxially oriented film to a heat treatment at 70 to 200° C. | 02-03-2011 |
20110104437 | VAPOR DEPOSITION FILM - A vapor deposition film has a vapor deposition layer composed of a metal or an inorganic oxide formed on at least one side of a resin layer (A) which is composed of a resin composition (1). The resin composition (1) is a polyglycol acid containing not less than 70% by mole of a specific structure (a structure represented by formula (1)) as a repeating unit. The surface on which the vapor deposition layer is deposited has a center line average roughness of 5-50 nm. The vapor deposition film has excellent gas barrier properties, excellent workability and decomposition resistance sufficient for practical use. | 05-05-2011 |
20120270048 | BIODEGRADABLE ALIPHATIC POLYESTER PARTICLES AND PRODUCTION PROCESS THEREOF - Biodegradable aliphatic polyester particles have: (A) an average particle diameter of 10 to 500 μm, and (B) a quantity of heat of low-temperature crystallization calculated as an exotherm attending on crystallization, detected in the course of heating by DSC, of at least 1 J/g, and preferably: (C) a quantity of heat of crystal melting calculated as an endotherm attending on melting of a crystal, detected in the course of the heating, of less than 100 J/g, and (D) a difference between the quantity of heat of crystal melting and the quantity of heat of low-temperature crystallization of less than 90 J/g. A process for producing the particles, comprises grinding a particular biodegradable aliphatic polyester having a weight average molecular weight of at least 50,000 at not lower than 0° C. and lower than the glass transition temperature of the polyester while applying high shearing force. | 10-25-2012 |
20130224485 | UNDRAWN POLYGLYCOLIC ACID-BASED RESIN YARN, DRAWN POLYGLYCOLIC ACID-BASED RESIN YARN USING THE SAME, AND METHODS FOR PRODUCING THE SAME - A method for producing an undrawn polyglycolic acid-based resin yarn, including: a discharge step of discharging a molten polyglycolic acid-based resin through a spinneret, to thereby form a fibrous polyglycolic acid-based resin; a keeping step of keeping the fibrous polyglycolic acid-based resin for 0.0012 seconds or more after the discharge in an atmosphere having a temperature of not lower than 110.5° C. but not higher than a melting point of the polyglycolic acid-based resin; and a cooling step of cooling the fibrous polyglycolic acid-based resin obtained in the keeping step, to thereby obtain an undrawn polyglycolic acid-based resin yarn. | 08-29-2013 |
20130252854 | OIL DRILLING AUXILIARY DISPERSION - A dispersion liquid for supporting oil drilling, including: an aqueous medium and a particulate solid polyglycolic acid resin dispersed in the aqueous medium; wherein the particulate polyglycolic acid resin has a weight-average molecular weight of at least 70,000 and at most 500,000, and exhibits weight retentivities in water at 80° C. of at least 85% after 12 hours, at most 80% after 72 hours, and at most 45% after 168 hours. The particulate solid polyglycolic acid resin included in the above-mentioned dispersion liquid for supporting oil drilling, functions as a fluidity control material exhibiting ideal degradation characteristics in the drilling operation for expansion of oil production capacity, demanded for suppressing the liquid permeability in the early stage and recovery of the liquid permeability after completion of the operation of the formation around the oil well. | 09-26-2013 |
20140017495 | Biodegradable Aliphatic Polyester Particles and Production Process Thereof - The invention provides biodegradable aliphatic polyester particles having the following physical properties: (A) the average particle diameter thereof is 5 to 500 μm; and (B) the fracture stress of a columnar tablet obtained by molding the particles in a cylindrical mold by applying a load of 4 kgf/cm | 01-16-2014 |
20150072903 | OIL DRILLING AUXILIARY DISPERSION - A dispersion liquid for supporting oil drilling, including: an aqueous medium and a particulate solid polyglycolic acid resin dispersed in the aqueous medium; wherein the particulate polyglycolic acid resin has a weight-average molecular weight of at least 70,000 and at most 500,000, and exhibits weight retentivities in water at 80° C. of at least 85% after 12 hours, at most 80% after 72 hours, and at most 45% after 168 hours. The particulate solid polyglycolic acid resin included in the above-mentioned dispersion liquid for supporting oil drilling, functions as a fluidity control material exhibiting ideal degradation charateristics in the drilling operation for expansion of oil production capacity, demanded for suppressing the liquid permeability in the early stage and recovery of the liquid permeability after completion of the operation of the formation around the oil well. | 03-12-2015 |
20150126414 | POLYGLYCOLIC ACID RESIN SHORT FIBERS AND WELL TREATMENT FLUID - PGA short fibers having the following characteristics of (a) to (c): (a) strength of 1 to 20 gf/D; (b) a mass loss of at least 10% after 14 days in water at a temperature of 60° C.; and (c) a pH of 1 to 5 after 3 days in water at a temperature of 60° C. with a solid content concentration of 2 mass %. The PGA short fibers preferably further having (d1) an outside diameter of 1 to 120 μm, (e1) a fiber length of 2 to 30 mm, and (f1) a fineness of 0.1 to 25 D, or the PGA short fibers preferably further having (d2) an outside diameter of 1 to 200 μm, (e2) a fiber length of less than 2 mm, and (f2) an aspect ratio of 2 to 1,200. Also, a well treatment fluid containing the PGA short fibers. | 05-07-2015 |